MOLYDBENUM
Basic information:
Material pure molybdenum wire 99.95%
Surface: Graphite coated
Size: 3.17mm, 2.00mm, 1.6mm
Application:
Thermal spray coating
H.S. Code 810296000
Product description:
Molybdenum wire used for thermal spray application is a pure(99.95%) molybdenum wire specifically designed for spraying. It produces dense, well bonded coating with excellent wear resistance and good corrosion resistance. It is particularly effective for applications where scuffing or galling is a problem such as piston rings, shift forks and synchronizing rings.
Application:
1. Wear Resistant coatings
2. Corrosion Resistance
3. Anti Galling
4. Bond Coatings
Typical Deposit Characteristics
| Hardness HRC | Bond strength | Deposit Rate | Deposit efficiency | Wire coverage | Surface texture |
| 15-20 | 7900psi | 10lbs/hr/100a | 75% | 1.1 oz/ft2/m | variable |
Surface preparation
Surface should be clean white metal with no oxide(rust), dirt, grease, or oil on the surface to be coated. Note; it is best not to handle surfaces after cleaning.
Recommended method of preparation is to girt blast with 24 mesh aluminium oxide, rough grind rough machine in a lathe.
Chemical Composition
MO 99.95%
Recommended spray parameters
| Diameter | Air pressure | Voltage | Amperage | Standoff |
| 1.6mm | 50-60psi | 32-34 | 100-250 | 3-7in(7-17cm) |
Parameters are typical and may vary depending on equipment used. Contact your equipment manufacturer for optimum spray parameters.